Midziyo yesimbi

Tsananguro Pfupi:

Metal powders isimbi idzo dzakaderedzwa kuita dzakatsetseka zvikamu uye ndidzo dzekutanga zvigadzirwa zvekutanga zveiyo 3D kudhinda maitiro ayo anogadzira esimbi zvikamu. 3D kudhinda, inozivikanwawo seyekuwedzera yekugadzira (AM), ndiko kugadzirwa kwezvikamu uye zvigadzirwa mune yakasarudzika-ne-yakatenderera fashoni. Ose maitiro eiyo simbi hupfu uye mhando yeiyo 3D yekudhinda maitiro anoona zvivakwa zveyekupedzisira chigadzirwa. Unhu hwehupfu hunotora nzvimbo zvichienderana nenzira yaunogadzirwa nayo, izvo zvinogona kuzokonzeresa kuita kwakasiyana kwemaitiro morphology uye kuchena.

Tumira neindaneti kwatiri Dhawunirodha sePDF

Chigadzirwa Chigadzirwa

Chigadzirwa Mateki

Stainless Simbi, Type ； 316L
Hunhu hwepanyama	hukuru hukuru	15-53 μm
	Chimiro	Idenderedzwa
	kuyerera	40 S (Imba inoyerera mita)
	kuoneka kuwanda	3.9 g / cm3
	Kuwandisa	7.98 g / cm3

Kemikari Kuumbwa	Fe	Chasara
	Cr	16 ～ 18 wt%
	Ni	10 ～ 14 wt%
	Mo	2 ～ 3 wt%
	Mn	W2 wt%
	Si	W1 wt%
	C	≤0.05 wt%
	P	≤0.045 wt%
	S	≤0.03 wt%
	O	≤0.1 wt%

Zvikamu zvezvivakwa	Kuwanda kwehukama	Approx. 99.9%
	Tensile simba	Approx. 560 MPa
	Bvisa simba	Kubata. 480 MPa
	Elongation mushure mekuputsika	Kubata. 20%
	Elasticity modulus	Kubata. 180 GPa
	Kuoma	Kubata. 85 HRB (158 HB)

Aluminium chiwanikwa, Type: AlSi10Mg
Hunhu hwepanyama	hukuru hukuru	15-53 μm
	Chimiro	Idenderedzwa
	kuyerera	150 S (Imba inoyerera mita)
	kuoneka kuwanda	1,45 g / cm3
	Kuwandisa	2,67 g / cm3

Kemikari Kuumbwa	Al	Chasara
	Si	9 ～ 10 wt%
	Mg	0.2 ～ 0.45 wt%
	Cu	≤0.05 wt%
	Mn	≤0.45 wt%
	Ni	≤0.05 wt%
	Fe	≤0.55 wt%
	Ti	≤0.15 wt%
	C	0.0075wt%

Zvikamu zvezvivakwa	Kuwanda kwehukama	≥95%
	Tensile simba	Approx. 330 MPa
	Bvisa simba	Approx. 245 MPa
	Elongation mushure mekuputsika	Approx. 6%
	Elasticity modulus	Approx. 70 GPa
	Kuoma	Approx. 120 HB

Titanium chiwanikwa, Type: TC4 (Ti-6Al-4V)
Hunhu hwepanyama	hukuru hukuru	15-45 μm
	Chimiro	Idenderedzwa
	kuyerera	45 S (Imba inoyerera mita)
	kuoneka kuwanda	2.5 g / cm3
	Kuwandisa	4.51 g / cm3

Kemikari Kuumbwa	Ti	Chasara
	Al	5 ～ 6.75 wt%
	V	3.5 ～ 4.5 wt%
	Fe	≤0.25 wt%
	C	≤0.02 wt%
	Y	≤0.005 wt%
	O	0.14, 0.16 wt%
	N	≤0.02 wt%
	Cu	≤0.1 wt%
	Zvimwe	0.4 wt%

Zvikamu zvezvivakwa	Kuwanda kwehukama	Approx.99.9%
	Tensile simba	Kubata. 1000 MPa
	Bvisa simba	Kubata. 900 MPa
	Elongation mushure mekuputsika	Approx. 10%
	Elasticity modulus	Kubata. 110 GPa
	Kuoma	Kubata. 300 HV (294 HB)

Nickel-base superalloy Rudzi: IN718
Hunhu hwepanyama	hukuru hukuru	15-53 μm
	Chimiro	Idenderedzwa
	kuyerera	40 S (Imba inoyerera mita)
	kuoneka kuwanda	4.1 g / cm3
	Kuwandisa	8.15 g / cm3

Kemikari Kuumbwa	Ni	50 ～ 55 wt%
	Cr	17 ～ 22 wt%
	Nb	4.75 ～ 5.5 wt%
	Mo	2.8 ～ 3.3 wt%
	Co	W1 wt%
	C	≤0.08 wt%
	P	≤0.015 wt%
	Si	≤0.35 wt%
	Al	0.2 ～ 0.8 wt%
	Ti	0,65 ～ 1,15 wt%
	Fe	Chasara

Zvikamu zvezvivakwa	Kuwanda kwehukama	≥99%
	Tensile simba	Approx. 980 MPa (1240 MPa mushure mekurapa kwekupisa)
	Bvisa simba	Approx. 780 MPa (1000 MPa mushure mekurapa kwekupisa)
	Elongation mushure mekuputsika	12 ～ 30%
	Elasticity modulus	Approx. 160 GPa
	Kuoma	Approx. 30 HRC (47 HRC mushure mekurapa kwekupisa)

Simbi Yekutengesa, Type: MS1
Hunhu hwepanyama	hukuru hukuru	15-53 μm
	Chimiro	Idenderedzwa
	kuyerera	40 S (Imba inoyerera mita)
	kuoneka kuwanda	4.3 g / cm3
	Kuwandisa	8 g / cm3

Kemikari Kuumbwa	Fe	Chasara
	Co	8.5 ～ 9.5 wt%
	Ni	17 ～ 19 wt%
	Mo	4.2 ～ 5.2 wt%
	Mn	≤0.1 wt%
	Ti	0.6 ～ 0.8 wt%
	C	≤0.03 wt%
	Al	0.05 ～ 0.15 wt%
	S	≤0.01 wt%
	Cr	≤0.3 wt%

Zvikamu zvezvivakwa	Kuwanda kwehukama	≥99%
	Tensile simba	Arrpox. 1090 MPa (1930 MPa mushure mekurapa kwekupisa)
	Bvisa simba	Arrpox. 1000 MPa (1890 MPa mushure mekurapa kwekupisa)
	Elongation mushure mekuputsika	Arrpox. 4%
	Elasticity modulus	Arrpox. 160 GPa (180 GPa mushure mekurapa kwekupisa)
	Kuoma	Arrpox.35 HRC

Cobalt-chromium chiwanikwa, Type: MP1 (CoCr-2Lc)
Hunhu hwepanyama	hukuru hukuru	15-53 μm
	Chimiro	Idenderedzwa
	kuyerera	40 S (Imba inoyerera mita)
	kuoneka kuwanda	4.1 g / cm3
	Kuwandisa	8.3 g / cm3

Kemikari Kuumbwa	Co	Chasara
	Cr	26 ～ 30 wt%
	Mo	5 ～ 7 wt%
	Si	W1 wt%
	Mn	W1 wt%
	Fe	≤0.75 wt%
	C	≤0.16 wt%
	Ni	≤0.1 wt%

Zvikamu zvezvivakwa	Kuwanda kwehukama	≥99%
	Tensile simba	Kubata. 100 MPa
	Bvisa simba	Kubata. 900 MPa
	Elongation mushure mekuputsika	Approx. 10%
	Elasticity modulus	Kubata. 200 GPa
	Kuoma	35 ～ 45 HRC (323 ～ 428 HB)